PARTS CLEANING process has two soak cleans, an HCL acid rinse and then an electrode clean. We have better results with the electrode clean current off than with it on. We have checked the current and it is reversed. Why is this?—D.P. A. Since you do not mention the polarity or type of electrocleaning, I am not sure what you mean by saying that the current is reversed. There are two categories of electrocleaning. The more popular type is anodic or reversecurrent electrocleaning, since it is actually dissolving some amount of the base material, avoids the deposition of other metallic substrates on the surface and also avoids hydrogen generation at the surface that can lead to hydrogen embrittlement of higher-strength steels. Cathodic or direct-current electrocleaning has the advantage of generating twice as much hydrogen at the surface as the amount of oxygen generated from the anodic process. As mentioned, it also has the disadvantage of "plating" bath impurities onto the surface and requiring that higher-strength steels have a one-hour bake to avoid hydrogen embrittlement. Based on the problem you are experiencing, you may be performing the cathodic process on your parts and they are either getting passivated from this process and/ or having some deposits form on the surface that gives the appearance that it is worse than cleaning without current at all. I recommend you attempt to change the current direction to perform an anodic cleaning, which will hopefully yield improved results. An alternative would be mixing the processes into what is known as periodic reverse electrocleaning. In this case, you will alternate applying cathodic and anodic electrocleaning. It is typical to end the process with the anodic or reverse electrocleaning process for the advantages listed above. CLINIC Turnkey Parts-Cleaning and Processing Systems Cleaning Nital Etching Steel and Titanium Etching Titanium and Aluminum Anodizing Pickling Chromating/Alodine Passivating Electropolish Chemical Polish for Steel Process design, equipment design and experienced world-wide installation ® www.miraclean.com 716.763.4343 Rinsing Q. In a dragout /rinsing process, is cold water effective or beneficial after a hot water rinse?—C.S. A. Additional rises are almost always beneficial to remove the "contaminant," whether it is residual cleaner, plating chemicals, etc. However, the final rinse is often the one that usually is reserved for the end of the line. This is because if you counterflow your rinse tanks, some of that heat will be picked up in the rinse tank it is flowing into. Additionally, heating the last tank can aid in the drying process, which is often necessary following most aqueous processing. Cleaning and Pretreatment Zone Have a question? Email David or check out our vast library of parts cleaning articles. pfonline.com/zones/clean. PRODUCTS FINISHING — pfonline.com 37